NBR Sheet (Acrylonitrile butadiene rubber)
【 Features 】
・Excels in oil resistance.
【 Applications 】
・Packing material for fuel.
*Hardness measurement is revised to “After 3 seconds” according to JIS K 6253 (2006). However, generally, the conventional "measurement within 1 second" is to be the mainstream for nominal hardness, so this result is measured value and the measurement result after 3 seconds is shown in ().
【 Properties: Black Rubber Sheet 】
| Item Name | Properties | ||||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| General Properties | Heat-Resistant Aging 100°C × 72h |
Oil Resistance 100°C × 72h |
Compression Set 100°C × 72h % |
Elastic Modulus in Static Shear MPa |
JIS K 6380 Corresponding No. |
Item Number |
|||||||
| Hardness Type A |
Tensile Strength at Break MPa {kgf/cm2} |
Elon gation at Break % |
Hardness Change Type A |
Change Rate of Tensile Strength % |
Change Rate of Elongation at Break % |
Volume Change Rate % |
|||||||
| ASTM #1 |
IRM 903 | ||||||||||||
| NBR Sheet-L | <50> | 51(50) | 8.1 {83} |
550 | +11 | +3 | -34 | -8 | +3 | 62 | BEH 50361 |
TNKL 5005 |
|
| <60> | 60(59) | 9.4 {96} |
560 | +11 | -15 | -44 | -7 | +32 | 75 | BEH 60351 |
TNKL 6005 |
||
| <70> | 70(67) | 12.2{124} | 550 | +6 | +2 | -43 | -13 | -1 | 67 | 1.15 | BFH 70341 |
TNKL 7007 |
|
| <80> | 82(77) | 8.4 {86} |
420 | +6 | +12 | -35 | -7 | +15 | 55 | BFH 80121 |
TNKL 8005 |
||
| <90> | 90(87) | 8.6 {88} |
360 | +3 | +18 | -6 | -4 | +5 | 55 | 1.48 | BFH 90321 |
TNKL 9007 |
|
| NBR Sheet-M | <30> | 33(27) | 10.8{110} | 1030 | +5 | -9 | -16 | -14 | +15 | 44 | BEH 30371 |
TNKM 3007 |
|
| <40> | 41(37) | 12.7{129} | 800 | +5 | -40 | -20 | -15 | +10 | 55 | BFH 40471 |
TNKM 4010 |
||
| <50> | 53(48) | 12.2{124} | 710 | +6 | +4 | -43 | -19 | +1 | 73 | BFH 50471 |
TNKM 5010 |
||
| <60> | 61(58) | 10.8{110} | 570 | +7 | -5 | -30 | -9 | +8 | 55 | BFH 60461 |
TNKM 6010 |
||
| NBR Sheet-H | <50> | 52(51) | 14.6{149} | 610 | +8 | -15 | -29 | -8 | +21 | 27 | BEH 50471 |
TNKH 5012 |
|
| <60> | 60(56) | 11.3{115} | 430 | +6 | 0 | -25 | -10 | -2 | 52 | BGH 60461 |
TNKH 6010 |
||
| <70> | 71(70) | 16.1{164} | 410 | +7 | -5 | -34 | -6 | +4 | 31 | BFH 70451 |
TNKH 7012 |
||
| <90> | 90(84) | 17.8{182} | 280 | +5 | +6 | -39 | -5 | +9 | 56 | BFH 90421 |
TNKH 9015 |
||
| Transformer NBR | <70> | 70(65) | 17.9{183} | 470 | +4 | +4 | -20 | -19 | +15 | 20 | BFH 70551 |
TNKH 7015 |
|
- JIS K 6250
【 Properties: Colored Rubber Sheet 】
| Item Name | Properties | ||||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| General Properties | Heat-Resistant Aging 100°C×72h |
Oil Resistance 100°C × 72h |
Compression Set 100°C × 24h |
Elastic Modulus in Static Shear MPa |
JIS K 6380 Corresponding No. |
Item Number |
|||||||
| Hardness Type A |
Tensile Strength at Break MPa {kgf/cm2} |
Elon- gation at Break % |
Hardness Change Type A |
Change Rate of Tensile Strength % |
Change Rate of Elongation at Break % |
Volume Change Rate % |
|||||||
| ASTM #1 |
IRM 903 | ||||||||||||
| White NBR Sheet-L | <50> | 50(47) | 11.1{113} | 690 | +2 | -27 | -21 | -4 | +31 | 30 | BEH 50360 |
TNWL 5005 |
|
| <65> | 65(63) | 8.9 {91} |
710 | +2 | -23 | -17 | +3 | +36 | 25 | 0.84 | BEH 65350 |
TNWL 6507 |
|
- JIS K 6250
【 Properties: Weather Resistant Rubber Sheet 】
| Item Name |
Properties | ||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|
| General Properties | Heat-Resistant Aging 100°C×72h |
Oil Resistance 100°C×72h |
Comp- ression Set 100°C × 72h % |
JIS K 6380 Corresponding No. |
Item Number |
||||||
| Hardness Type A |
Tensile Strength at Break MPa {kgf/cm2} |
Elon- gation at Break % |
Hardness Change Type A |
Change Rate of Tensile Strength % |
Change Rate of Elongation at Break % |
Volume Change Rate% |
|||||
| ASTM #1 |
IRM 903 |
||||||||||
| TNB6007-O | 59(56) | 9.6 {98} |
510 | +4 | +3 | -21 | -10 | +9 | 45 | BFH 60331 |
TNKM 6007-O |
| TNB9007-O | 90(81) | 9.9 {101} |
400 | +3 | +16 | -35 | -2 | +17 | 59 | BFH 90321 |
TNKM 9007-O |
JIS K 6250
【 Properties: Gasoline Resistant Rubber Sheet 】
| Item Name | Properties | |||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|
| General Properties | Heat-Resistant Aging 100°C×72h |
Oil Resistance | Comp- ression Set 100°C × 72h % |
JIS K 6380 Corresponding No. |
Item Number |
|||||||
| 25°C × 72h |
100°C × 72h |
|||||||||||
| Hardness Type A |
Tensile Strength at Break MPa {kgf/cm2} |
Elon- gation at Break % |
Hardness Change Type A |
Change Rate of Tensile Strength % |
Change Rate of Elon- gation at Break % |
Volume Change Rate % |
||||||
| Gasoline | IRM 903 |
|||||||||||
| NBR-G | <70> | 73 (71) | 18.2 {186} |
280 | +7 | -3 | -40 | +9 | -2 | 34 | BGH 70451 |
TNKL 7010-E |
JIS K 6250
•These products should not be incinerated wherever possible because harmful gas to humans might be generated if they are immoderately burned.
•The user is requested to confirm degree of discoloration and contamination by using sample in the case of use contacting with the other items.
•The life of these products at actual use are greatly affected by condition of the use. The user is requested to confirm it by using sample in the case of use under severe condition.
●These descriptions can be altered for a reason of improvement without any notification.