Function, rubber sheet according to a use
Conductive Rubber Sheet
EP Sheet (EP-2 Type, EP-5 Type)
【 Type 】
EP-2 | Resistivity Value 102Ω•cm Type (Material : 3 types : Natural rubber, CR system, NBR system) |
---|---|
EP-5 | Resistivity Value 105Ω•cm Type (Material : 3 types : Natural rubber, CR system, NBR system) |
*Hardness measurement is revised to “After 3 seconds” according to JIS K 6253 (2006). However, generally, the conventional "measurement within 1 second" is to be the mainstream for nominal hardness, so this result is measured value and the measurement result after 3 seconds is shown in ().
【 Properties: EP Sheet 】
Properties | Item Name | |||||||
---|---|---|---|---|---|---|---|---|
Unit | EP-2 | EP-5 | ||||||
REP-2 (Natural Black Rubber) |
CEP-2 (CR Black Rubber) |
NEP-2 (NBR Black Rubber) |
REP-5 (Natural Black Rubber) |
CEP-5 (CR Black Rubber) |
NEP-5 (NBR Black Rubber) |
|||
General Properties |
Hardness | TypeA | 65(65) | 62(60) | 72(69) | 72(72) | 72(71) | 73(71) |
Tensile Strength at Break |
MPa {kgf/cm2} |
15.7 {161} |
12.5 {128} |
21.3 {217} |
16.2 {166} |
12.0 {123} |
9.9 {101} |
|
Elongation at Break |
% | 410 | 310 | 430 | 310 | 230 | 250 | |
Heat Aging Resistance |
― | Test Condition |
70°C×72h | 100°C×72h | 100°C×72h | 70°C×72h | 100°C×72h | 100°C×72h |
Hardness Change |
TypeA | +6 | +18 | +8 | +3 | +16 | +10 | |
Change Rate of Tensile Strength at Break |
% | -15 | -10 | -4 | -5 | -2 | +6 | |
Change Rate of Elongation at Break |
% | -33 | -40 | -32 | -24 | -49 | -42 | |
Compression Set | Test Condition |
70°C×24h | 100°C×72h | 100°C×72h | 70°C×24h | 100°C×72h | 100°C×72h | |
% | 20 | 35 | 34 | 13 | 35 | 47 | ||
Oil Resistance |
― | Test Condition |
70°C×24h | 100°C×72h | 100°C×72h | 70°C×24h | 100°C×72h | 100°C×72h |
ASTM #1 Volume Change Rate |
% | ― | +13 | -3 | ― | +19 | -1 | |
IRM 903 Volume Change Rate |
% | ― | +92 | +28 | ― | +95 | +29 | |
Volume Intrinsic Resistivity |
Before Heat Aging |
Ω•cm | 0.9×102 | 1.2×102 | 1.2×102 | 5.1×104 | 1.4×104 | 8.6×104 |
After Heat Aging |
Test Condition |
70°C×24h | 100°C×72h | 100°C×72h | 70°C×24h | 100°C×72h | 100°C×72h | |
Ω•cm | 1.2×102 | 0.5×102 | 1.7×102 | ― | ― | ― |
- JIS K 6250
- ●Thickness of the product is 1-5mm.
- ●Please consult us for a conductivity depends on its usage.
EC Sheet : Consists of sheet of one color.
ECC - 8 Sheet : Consists of laminate of colored sheet (1mm) and black colored sheet.

【 Properties: EC Sheet / ECC-8 Sheet 】
Properties | Unit | Item Name | |
---|---|---|---|
EC-8 (ECC-8) | |||
Hardness | Type A | 70(62) | |
Oil Resistance | ASTM #1 Volume change Rate | % | +1 |
IRM 903 Volume change Rate | % | +35 | |
Volume Intrinsic resistivity | before aging | Ω•cm | 7.9 × 108 |
after aging 70°C×72h | Ω•cm | 2.5 × 108 |
【 Dimension 】
Item Name | Thickness (mm) |
Width (m) |
Length (m) |
Color Standard |
---|---|---|---|---|
EC | 1-3 | 1 | 10 | Green |
ECC | 2-3 | 1 | 10 | Green |
EC-8N (Cloth-inserted) Sheet Resistivity Value 108Ω•cm Type
【 Features 】
・Construction without back or front making it free of "distortion" and "warpage" caused by prolonged use.
・In addition to the high surface hardness, polyester cloth is filled in the middle making the movement of asters and trucks smooth.
・NBR formulation makes it excellent in oil resistance and chemical resistance.
【 Structure 】

【 Dimension 】
Item Name | Thickness(mm) | Width(m) | Length(m) | Color Standard |
---|---|---|---|---|
EC-8N | 2 | 1 | 10 | Green |
3 | 1 | 10 | Green |
●Please consult us on the other colors and sizes
EC - 8H Sheet
【 Features 】
・Optimum hardness against writing instrument pressure.
・EC-8H Sheet is a colored type with white as standard.
・High in surface hardness making the movement of casters and trucks smooth.
【 Applications 】
・Drawing board of automatic drafting machine.
・Suited for tables and etc. to write words.
【 Structure 】

Item Name | Properties | |||
---|---|---|---|---|
General Properties | Volume Intrinsic Resistivity Ω•cm |
|||
Hardness Type A | Tensile Strength at Break MPa{kgf/cm2} |
Elongation at Break % |
||
EC-8H | 95(93) | 9.4 {96} | 160 | 6×109 |
JIS K 6250
【 Dimension 】
Item Name | Thickness(mm) | Width(m) | Length (m) | Color Standard |
---|---|---|---|---|
EC-8H | 1-3 | 1 | 10 | White |

![]() |
Volume Intrinsic Resistivity Resistance which depends on object type at carrying an electric current through inside of the object. Defined with resistance between facing sides of cubic. Unit: Ω•cm |
![]() |
Surface Intrinsic Resistivity Resistance which depends on object type and surface condition at carrying an electric current through a surface of the object. Defined with resistance between facing sides of square. Unit: Ω |
●These descriptions can be altered for a reason of improvement without any notification.
●These descriptions shall be as of November 1, 2021.