natural rubber
NR Sheet (Natural Rubber)
【 Features 】
•Excels in workability
【 Applications 】
•Rubber mat
【 Properties : Black Normal Sheet 】
| Item Name | Properties | ||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|
| General Properties | Heat-Resistant Aging 70°C×72h |
Compression Set 70°C×24h % |
Elastic Modulus in Static Shear MPa |
JIS K 6380 Corres- ponding No. |
Item Number |
||||||
| Hardness Type A |
Tensile Strength at Break MPa {kgf/cm2} |
Elongation at Break % |
Hardness Change Type A |
Change Rate of Tensile Strength % |
Change Rate of Elongation at Break % |
||||||
| Black Normal Sheet | <65> | 64(64) | 3.4{35} | 290 | +8 | +7 | -15 | 35 | 0.84 | AAH65133 | TAKL 6503 |
- JIS K 6250
- *These items highlighted in this color are our standard products.
【 Features 】
•Excels in mechanical
•Excels in abrasion resistance
•Excels in elasticity
【 Applications 】
•Rubber mat
【 Properties : Black Rubber Sheet Properties 】
| Item Name | Properties | ||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|
| General Properties | Heat-Resistant Aging 70°C×72h |
Compression Set 70°C×24h % |
Elastic Modulus in Static Shear MPa |
JIS K 6380 Corres- ponding No. |
Item Number |
||||||
| Hardness Type A |
Tensile Strength at Break MPa {kgf/cm2} |
Elongation at Break % |
Hardness Change Type A |
Change Rate of Tensile Strength % |
Change Rate of Elongation at Break % |
||||||
| Black Rubber Sheet (30%) |
<50> | 48(48) | 8.9{9.1} | 600 | +4 | +2 | -7 | 19 | AAH50153 | TAKL 5005 |
|
| <60> | 60(60) | 8.2{84} | 410 | +7 | +19 | -12 | 23 | AAH60363 | TAKL 6007 |
||
| <70> | 72(71) | 8.6{88} | 350 | +8 | -10 | -24 | 28 | AAH70343 | TAKL 7007 |
||
| <80> | 80(75) | 9.7{99} | 270 | +5 | -2 | -13 | 20 | AAH80323 | TAKL 8007 |
||
| <90> | 92(89) | 10.4{106} | 300 | +2 | +6 | -30 | 28 | AAH90323 | TAKL 9005 |
||
| Black Rubber Sheet (40%) |
<40> | 43(43) | 8.2{83.6} | 610 | +6 | +18 | +2 | 18 | AAH40373 | TAKM 4007 |
|
| <50> | 48(48) | 8.9{90.8} | 600 | +4 | +2 | -7 | 19 | 0.82 | AAH50373 | TAKM 5007 |
|
| <60> | 61(60) | 10.2{104} | 420 | +5 | +6 | -12 | 13 | AAH60463 | TAKM 6010 |
||
| <70> | 73(72) | 17.5{179} | 430 | +4 | -2 | -25 | 15 | AAH70453 | TAKM 7010 |
||
| Black Rubber Sheet | <50> | 50(50) | 19.1{195} | 550 | +5 | -10 | -17 | 14 | AAH50473 | TAKM 5010 |
|
| <60> | 56(56) | 22.2{226} | 470 | +2 | +9 | -20 | 13 | AAH60573 | TAKM 6012 |
||
- JIS K 6250
- *These items highlighted in this color are our standard products.
【 Properties : Colored Rubber Sheet Properties 】
| Item Name | Properties | ||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|
| General Properties | Heat-Resistant Aging 70°C×72h |
Compression Set 70°C × 24h % |
Elastic Modulus in Static Shear MPa |
JIS K 6380 Corres- ponding No. |
Item Number |
||||||
| Hardness Type A |
Tensile Strength at Break MPa {kgf/cm2} |
Elongation at Break % |
Hardness Change Type A |
Change Rate of Tensile Strength % |
Change Rate of Elongation at Break % |
||||||
| White Normal Sheet | <50> | 53(51) | 6.5{66} | 550 | +6 | +12 | -2 | 35 | AAH50153 | TAWL 5005 |
|
| <65> | 63(62) | 5.4{55} | 480 | +2 | 0 | -5 | 34 | 1.03 | AAH65143 | TAWL 6504 |
|
| <85> | 85(81) | 5.0{51} | 430 | +5 | -20 | -22 | 50 | AAH85142 | TAWL 8504 |
||
| White Rubber Sheet | <40> | 39(39) | 19.9{203} | 740 | +4 | -6 | -10 | 16 | AAH40573 | TAWM 4015 |
|
| <70> | 69(68) | 10.0{102} | 680 | -1 | -4 | -3 | 46 | AAH70363 | TAWL 7007 |
||
| Red Normal Sheet | <65> | 63(62) | 8.1{83} | 640 | +5 | +2 | -10 | 30 | AAH65253 | TARL 6504 |
|
| Green Normal Sheet | <70> | 68(68) | 8.7{89} | 570 | +4 | -5 | -5 | 29 | 1.29 | AAH70233 | TAML 7005 |
| Light-green Normal Sheet | <70> | 66(65) | 7.6{78} | 590 | +5 | +1 | -7 | 43 | AAH70233 | TAML 7004 |
|
| Blue Normal Sheet | <65> | 66(65) | 8.3{85} | 420 | +7 | -5 | -15 | 35 | AAH65233 | TABL 6504 |
|
| Gray Normal Sheet | <65> | 68(68) | 6.8{69} | 530 | +1 | -1 | -8 | 43 | AAH65133 | TAHL 6504 |
|
- JIS K 6250
- *These items highlighted in this color are our standard products.
【 Properties : Amber Natural Rubber Sheet Properties 】
| Item Name | Properties | |||||||||
|---|---|---|---|---|---|---|---|---|---|---|
| General Properties | Heat-Resistant Aging 70°C× 72h |
Compression Set 70°C× 24h % |
JIS K 6380 Corresponding No. |
Item Number |
||||||
| Hardness Type A |
Tensile Strength at Break MPa {kgf/cm2} |
Elongation at Break % |
Hardness Change Type A |
Change Rate of Tensile Strength % |
Change Rate of Elongation at Break % |
|||||
| Amber Rubber Sheet(40%) | <50> | 48(47) | 11.8{120} | 640 | +3 | +5 | -7 | 14 | AAH50373 | TAAL 5007 |
| Amber Rubber Sheet(60%) | <45> | 47(47) | 19.1{195} | 680 | +2 | -6 | -5 | 19 | AAH45573 | TAAH 4512 |
- JIS K 6250
•These products should not be incinerated wherever possible because harmful gas to humans might be generated if they are immoderately burned.
•The user is requested to confirm degree of discoloration and contamination by using sample in the case of use contacting with the other items.
•The life of these products at actual use are greatly affected by condition of the use. The user is requested to confirm it by using sample in the case of use under severe condition.
●These descriptions can be altered for a reason of improvement without any notification.
●These descriptions shall be as of January 1, 2017.